TECHNICAL SPECIFICATIONS
  Fire Clay Bricks & High Alumina Bricks
  High Alumina, Sillimanite & Dense Bricks
  Castables
  Fire Clay & High Alumina Mortor
FIRE CLAY BRICKS & HIGH ALUMINA BRICKS
Product
& Brand Name
AL2O3
%
Min.

FE2O3
%
Min.

A.P.
%
Min.
B.D.
(Gm/ccs)
Min.
C.C.S.
(Kgf/Cm2)
Min.
P.C.E.
(O° C)
Min.
R.U.L.
(Ta°C)
Min.
P.L.C.
%
Max.
JASDAN-30
(IS:6)
30
2.20
25
1.90
250
31.00
1350
+ 1.5 at
1350°C/2 Hrs.
JASDAN-37
(HHD)
37
2.50
23
2.00
300
31.50
1370
+ 1.5 at
1400°C/2 Hrs.
JASDAN-40
(IS:8)
40
2.50
23
2.10
350
32.00
1400
+ 1.0 at
1450°C/2 Hrs.
JASDAN-45
45
2.60
21
2.20
370
32.00
1420
+ 1.5 at
1450°C/2 Hrs.
JASDAN-50
50
2.75
23
2.30
400
32.50
1430
+ 1.5 at
1450°C/2 Hrs.
JASDAN-55
55
2.90
23
2.40
400
33.00
1440
+ 1.5 at
1450°C/2 Hrs.
SHUBH-60
60
3.00
23
2.55
430
34.00
1450
+ 1.5 at
1500°C/2 Hrs.
SHUBH-65
65
3.00
23
2.60
450
34.50
1460
+ 2.0 at
1500°C/2 Hrs.
SHUBH-70
70
3.20
23
2.65
500
35.00
1470
+ 2.0 at
1500°C/2 Hrs.
SHUBH-75
75
3.40
22
2.70
600
36.00
1480
+ 2.5 at
1500°C/2 Hrs.
SHUBH-80
80
3.50
21
2.75
600
37.00
1500
+ 2.5 at
1550°C/2 Hrs.
NOTE:
1. SIZE TOLERANCE : + 1.5% OR 2mm whichever is greater
2. SHAPING DRY PRESSING.
3. THE ABOVE DATA ARE ON AVERAGE RESULT BASIS
 